NSF饮用水处理HDPE, NSF饮用水处理, 管道系统，NSF 14，NSF 61，管路挤出成型，挤出

 

PEXIDAN® L/T Eclipse

高密度聚乙烯

SACO AEI Polymers

Technical Data

 

产品说明

High density moisture-curable PE compound for hot & cold water plumbing pipe. Suitable for DR 9 pipe applications in continuous service at operating conditions of 140°F and 80 psi.

 

PEXIDAN® L/T (including L/T-UV and L/T Eclipse) is a high density PEX system consisting of a silane grafted base compound A-1001 and a catalyst masterbatch CAT-003 (or A-1022 and CAT-117). When mixed and extruded in the proper proportions, the two-component system results in a material that is crosslinkable by exposure to moisture or by immersion in hot water at 90-95°C. PEXIDAN® L/T is listed by NSF International to standards 14 and 61 and to Canadian Standards Association standard B137.5. NSFI certification to ASTM F876 and ASTM F2023 testifies to its superior resistance to oxidation by hot, chlorinated water. PEXIDAN® L/T is permitted to be used in domestic continuous re-circulation systems and is listed by NSF as a NSF-pw CL5 / PEX 5006 material.

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet (English)

搜索 UL 黄卡 • SACO AEI Polymers

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

特性 • 高密度 • 抗氧化 • 可交联

用途 • 管道系统

机构评级 • ASTM F2023 • CSA B137.5 • NSF 61

• ASTM F876 • NSF 14

形式 • 粒子

加工方法 • 管路挤出成型 • 挤出

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 3 0.948 0.946g/cm³ ASTM D792

熔流率（熔体流动速率） (190°C/2.16 kg) 0.70g/10 min 0.70g/10 min ASTM D1238

交叉结合的程度 70% 70% ASTM D2765

机械性能 额定值(英制) 额定值(公制) 测试方法

拉伸模量 ISO 527-1

-40°F (-40°C) 335000psi 2310MPa

32°F (0°C) 245000psi 1690MPa

73°F (23°C) 125000psi 862MPa

抗张强度 ASTM D638

屈服, 73°F (23°C) 3100psi 21.4MPa

屈服, 180°F (82°C) 1630psi 11.2MPa

屈服, 199°F (93°C) 1260psi 8.69MPa

断裂, 73°F (23°C) 3430psi 23.6MPa

断裂, 180°F (82°C) 1740psi 12.0MPa

断裂, 199°F (93°C) 1740psi 12.0MPa

伸长率 ASTM D638

屈服, 73°F (23°C) 9.0% 9.0%

屈服, 180°F (82°C) 12% 12%

屈服, 199°F (93°C) 14% 14%

断裂, 73°F (23°C) 240% 240%

断裂, 180°F (82°C) 200% 200%

断裂, 199°F (93°C) 240% 240%

弯曲模量 ISO 178

-40°F (-40°C) 75000psi 517MPa

32°F (0°C) 55000psi 379MPa

73°F (23°C) 30000psi 207MPa

 

PEXIDAN® L/T Eclipse

高密度聚乙烯

 

SACO AEI Polymers

机械性能 额定值(英制) 额定值(公制) 测试方法

流体静力学设计基础 - @ 68% DOC ASTM D2837

73°F (23°C) 1250psi 8.62MPa

180°F (82°C) 800psi 5.52MPa

200°F (93°C) 630psi 4.34MPa

热性能 额定值(英制) 额定值(公制) 测试方法

维卡软化温度 255°F 124°C ASTM D1525

线形热膨胀系数 - 流动 8.3E-5in/in/°F 1.5E-4cm/cm/°C ASTM D696

(-148 到 185°F (-100 到 85°C))

比热 (73°F (23°C)) 0.459Btu/lb/°F 1920J/kg/°C

氧感应时间 (428°F (220°C)) > 50min > 50min ASTM D3895

补充信息 额定值(英制) 额定值(公制) 测试方法

Hot Elongation 4 内部方法

elongation under load : 302°F (150°C) 30% 30%

permanent elongation (set) after cooling : 0.0% 0.0%

302°F (150°C)

挤出 额定值(英制) 额定值(公制)

料筒 1 区温度 320 到 350°F 160 到 177°C

料筒 2 区温度 320 到 350°F 160 到 177°C

料筒 3 区温度 320 到 350°F 160 到 177°C

料筒 4 区温度 320 到 350°F 160 到 177°C

料筒 5 区温度 365°F 185°C

口模温度 365°F 185°C

 

 

 

 