RODRUN LC-5130G
液晶聚合物
UNITIKA Plastics Division
Technical Data
产品说明
Unitika Rodrun is a thermoplastics for percision injection classified into semi-aromatic liquid crystal polyesters (LCPs). LC-5000 series has a excellent moldability (high flow without flash, using a mold of low temperature) and precision (low warpage).
LC-5000 series are suitable for almost all dipping soldering conditions and partial reflow soldering (low warpage).
LCP has stiff molecular structure to form liquid crystal at molten stage. The archeological properties of low viscosity under shear stress gives high flow without flash problems. Rodrun which use a standard mold temperature of 40°C shows the rheological merit of LCP clearly.
Out shape of a LCP seem to be just like a normal plastics, however, the solid LCP consists of crystal and glasified liquid crystal. Rodrun has a low crystalinity in the mold. This property yields low shrinkage and low warpage. Rodrun is a suitable resin for precision parts.
总体
材料状态 • 已商用:停售
资料 1 • Technical Datasheet (English)
Search for UL Yellow Card • UNITIKA Plastics Division
• RODRUN
供货地区 • 亚太地区
填料/增强材料 • 玻璃纤维增强材料, 30% 填料按重量
• 半结晶 • 良好的成型性能 • 气体阻隔性
性能特点 • 低翘曲性 • 流动性高
• 收缩性低
• 低粘度 • 耐化学性良好
用途 • 工程配件 • 开关
加工方法 • 注射成型
物理性能 额定值单位制 测试方法
比重 1.61g/cm³ ASTM D792
吸水率 (23°C, 24 hr) 0.010% ASTM D570
机械性能 额定值单位制 测试方法
抗张强度 (屈服, 3.20 mm) 127MPa ASTM D638
伸长率 (断裂) 2.5% ASTM D638
弯曲模量 ASTM D790
1.60 mm 16700MPa
3.20 mm 12700MPa
弯曲强度 ASTM D790
屈服, 1.60 mm 191MPa
屈服, 3.20 mm 171MPa
冲击性能 额定值单位制 测试方法
无缺口悬臂梁冲击 98J/m ASTM D256
热性能 额定值单位制 测试方法
热变形温度 ASTM D648
0.45 MPa, 未退火 250°C
1.8 MPa, 未退火 225°C
可燃性 额定值单位制 测试方法
UL 阻燃等级 UL 94
0.800 mm HB
3.20 mm HB
注射 额定值单位制
干燥温度 130°C
干燥时间 4.0hr
料筒温度 120°C
螺筒后部温度 270°C
1 / 3 文件号: TDS-120040-zh
RODRUN LC-5130G
液晶聚合物
UNITIKA Plastics Division
注射 额定值单位制
螺筒中部温度 280°C
螺筒前部温度 290°C
射嘴温度 290°C
模具温度 40.0°C
备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料;不过您可以从供应商处了解最新资料。
2 一般属性:这些不能被视为规格。
|